Featured Product

Applications

Directions to Use

Clean surface / object properly by thinner as pretreatment system. After cleaning do the phosphating.

Apply one coat H. B. Z/P P S Grey, kindly note that DFT of this coat should be more than 40 microns.

For curing this coat required 8 to 10 hrs. at R. T. or by forced dry (Oven baking) at 80 to 90 °c for 20 min.

Apply P. U. Paint & maintain DFT of this coat 30 – 40 micron

Curing time of this paint takes 8 to 10 hrs. It required force dry temp is 80 - 90 °c for 20 min.

STOVING AUTO FINISH

Product Specifications

Physical Properties (Liquid Paint) : -

Composition		Pigments Alkyd Amino base
Specific Gravity		1.10 ( ± 0.05)Kg. Per Lit.
Non volatile matter		(50% - 65%) by weight
Flash point		+23 ° c
Fineness of grinding		+7 (Hegman Guage)
Supply viscosity		70 (± 5) Sec By Cup at Room Temp.
Thinner Intake		Maximum 40% by volume
Application Viscosity		20-25 Sec. ( By B-4 Viscosity Cup) at Room Temp
Flash off		10 minutes
Baking		130 (± 5 °c) for 30 minutes

DRY FILM PROPERTIES

Finish		Smooth & Gloosy
Shade		As per Standard
D.F.T.		20-25 micron. Per coat
Hardness		Pencil Hardness : HB, Scratch Hardness : 1000gm
Glossy		80 ( ± 5 ) unit at an angle 60 °
Flexibility		1/8”(No cracking, elongation & Gloss reduction)
Adhesion		100% passes (cross-cut)
Impact		500 gms (at 50 cms)
Sand ability		No Clogging of emery paper or damage to painted surface when Dry or wet sanded with emery paper 400 grade
Solvant Resistance		No dissolving, peeling, blistering, cracking & Loss of adhesion
Petrol / Diesel Resistance		No discoloration cracks & Loss of adhesion loss of gloss
Acid Resistance (0.1 N H2SO4 )		No discoloration peeling, loss of gloss, dissolving out.
Alkali Resistance (0.1 N Na2SO4)		No discoloration peeling, loss of gloss, blister dissolving out.
Covering capacity		110 ± 10sq.fts. per liter per coat
Salt Spray		180 hrs. (For system) 5% Nacl
Moisture Resistance		240 hrs. at 98% R.H. at 49(±1) °c
Weathering Test		Testing cycles 4 hrs. UV rays at 55-60 °c 4hrs. Condensation at 45--50 °c for 400hrs. ( 10% glossy reduction accepted )